PHYSICAL & MECHANICAL PROPERTIES |
APPARENT SPECIFIC DENSITY, kg/m3 (ASTMC-97) |
|
WATER ABSORPTION % wt (ASTM C-97) |
COMPRESSIVE STRENGTH, MPa (ASTM C-170) |
MODULUS OF RUPTURE UNDER FLEXURE(FLEXURAL STRENGTH) – WET CONDITION, MPa (ASTM C-99) |
2705 |
|
0,11 |
95 |
15 |
ABRASION RESISTANCE, mm (DIN 52108 – 20 CYCLES) |
|
|
|
|
8,55 |
|
|
|
|
MINERALOGICAL COMPOSITION, % wt |
CALCITE |
96 |
DOLOMITE |
3
|
QUARTZ |
1 |
|
CHEMICAL ANALYSIS, % wt |
CaO |
55
|
MgO |
0,45
|
SiO2 |
0,06 |
Fe2O3 |
0,14
|
AI2O3 |
0,40
|
K2O |
0,04
|
Na2O |
0,03
|
MnO |
0,02
|
LOI |
42,76
|
|
|